Indications
◆ Coping ◆ Inlay ◆ Onlay ◆ Bridge ◆ Crown
Available in White Zirconia 98mm/95mm Puck
◆ 10mm 12mm 14mm 16mm 18mm 20mm 22mm 25mm
Chemical Composition
|
Y2O3 |
5.2-5.5 wt% |
|
AI2O3 |
0.05wt% |
|
SiO2 |
<0.002wt% |
|
Fe2O3 |
<0.002wt% |
|
Aging Properties |
Monoclinic Phase <20% |
|
Chemical Solubility |
≤2000hg.cm-2 |
Physical Properties
|
Sintered Density |
6.08 g/cm3 |
|
Flexural Strength |
≥1200 Mpa |
|
Translucency |
>40% |
|
Solubility(Acetic acid) |
≤100 ug/cm2 |
|
Radioactivity |
≤0.015Bq/g |
Zirae HT White, these are high translucent zirconia blanks used for monolithic or anatomically reduced anterior restorations and up to 3-unit bridges in the molar region. The high-performance ceramic combines the outstanding processing characteristics of zirconia with comparable translucency previously only known in lithium disilicate. The result is highly esthetic restorations with permanent strength and stability. Restorations are processed and fitted intraorally without additional cost using commercially available luting material.